| No. | PTHF 1000 | DEAEA (CB Diol) | HAD | Temperature | Solvent | Time | Color | Hardness | Tensile Strength | Tensile Strength Afther Hydrolysis | Antifouling | Note |
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| 1 | 0 | 95 | 5 | 60 | Chloroform | 18 | White | Hard | Not Bad | |||
| 2 | 20 | 75 | 5 | 80 | DMF | 18 | Yellow | Soft | Good | |||
| 3 | 5 | 90 | 5 | 60 | Chloroform | 18 | Yellow | Medium | Good | Heating to 100C | ||
| 4 | 0 | 95 | 5 | 60 | Chloroform | 18 | Yellow | Hard | Good | Heating to 100C | ||
| 5 | 40 | 50 | 10 | 80 | DMF | 18 | Yellow | Hard | Very Good | |||
| 6 | 20 | 70 | 10 | 80 | DMSO | 18 | Yellow | Medium | Good | |||
| 7 | 90 | 0 | 10 | 60 | Chloroform | 18 | White | Hard | Very Good | |||
| 8 | 85 | 5 | 10 | 60 | Chloroform | 18 | White | Hard | Very Good | |||
| 9 | 80 | 10 | 10 | 60 | Chloroform | 18 | White | Hard | Very Good | |||
| 10 | 70 | 20 | 10 | 60 | Chloroform | 18 | White | Hard | Very Good | |||
| 11 | 60 | 30 | 10 | 60 | Chloroform | 18 | White | Hard | Very Good | |||
| 12 | 40 | 50 | 10 | 60 | Chloroform | 18 | White | Hard | Very Good | Non-uniform | ||
| 13 | 20 | 70 | 10 | 60 | Chloroform | 18 | White | Hard | Very Good | Non-uniform | ||
| 14 | 100 | 0 | 0 | 60 | Chloroform | 18 | White | Very Soft | Very Good | |||
| 15 | 55 | 35(NCB) | 10 | 60 | Chloroform | 18 | White | Hard | Good | |||
| 16 | 0 | 90(NCB) | 10 | 60 | Chloroform | 18 | White | Hard | Very Good |
Hardness: Use nails Hard - No Scratches Medium - Light Scratches Soft - Deep Scratches Very Soft - Breaking
Tensile Strength: Use hand Very Good - No Elongation Good - Light Elongation Not Bad - Can Break Bad - Easy Break Very Bad - Crispy